Multipurpose contact adhesive based on polychloroprene rubber in flammable solvents, light in color and with high initial tack.
This glue has a very long open time as well as great ease of application.
It is used exclusively as a single component without the addition of Catalyst and essentially in 2-sided gluing.
Not suitable for plasticized PVC (migration), nor expanded or extruded polystyrene (solvent attack). Product used in shoemaking, upholstery, furnishing, layout, construction as well as many industrial areas.
TECHNICAL CHARACTERISTICS
|
CHEMICAL BASIS |
Glue based on polychloroprene rubber + resins dissolved in flammable organic solvents. |
|---|---|
|
COLOR |
Yellowish |
|
CONSISTENCY |
Liquid easily applied with a brush |
|
DENSITY (g/cm3) |
~ 0.82 g/cm3 |
|
DRY MATTER CONTENT |
~24.1% |
|
VISCOSITY |
~ 1900 mPa.s |
|
CHARACTERISTICS OF POLYMERIZED GLUE FILM |
Fairly firm and flexible glue film. Excellent adhesive properties on many materials. Good thermal resistance up to +80°C peak (specific tests required depending on the materials and intended use). Single-component glue to be used without adding isocyanate catalyst |
|
CONSUMPTION / DEPOSIT |
~ 120 to 140 g/m² wet per side, variable depending on the nature of the materials to be bonded and the application system |
|
SETTING SPEED |
Very good tack and initial setting upon display / Final setting 24 hours |
|
OPEN TIME |
? 4 hours (2-sided gluing) |
|
OPERATING TEMPERATURE |
? +15°C and ? +30°C |
Multipurpose contact adhesive based on polychloroprene rubber in flammable solvents, light in color and with high initial tack.
This glue has a very long open time as well as great ease of application.
It is used exclusively as a single component without the addition of Catalyst and essentially in 2-sided gluing.
Not suitable for plasticized PVC (migration), nor expanded or extruded polystyrene (solvent attack). Product used in shoemaking, upholstery, furnishing, layout, construction as well as many industrial areas.
TECHNICAL CHARACTERISTICS
|
CHEMICAL BASIS |
Glue based on polychloroprene rubber + resins dissolved in flammable organic solvents. |
|---|---|
|
COLOR |
Yellowish |
|
CONSISTENCY |
Liquid easily applied with a brush |
|
DENSITY (g/cm3) |
~ 0.82 g/cm3 |
|
DRY MATTER CONTENT |
~24.1% |
|
VISCOSITY |
~ 1900 mPa.s |
|
CHARACTERISTICS OF POLYMERIZED GLUE FILM |
Fairly firm and flexible glue film. Excellent adhesive properties on many materials. Good thermal resistance up to +80°C peak (specific tests required depending on the materials and intended use). Single-component glue to be used without adding isocyanate catalyst |
|
CONSUMPTION / DEPOSIT |
~ 120 to 140 g/m² wet per side, variable depending on the nature of the materials to be bonded and the application system |
|
SETTING SPEED |
Very good tack and initial setting upon display / Final setting 24 hours |
|
OPEN TIME |
? 4 hours (2-sided gluing) |
|
OPERATING TEMPERATURE |
? +15°C and ? +30°C |